Basic Info.
Model NO.
FeCrAl
Ualloy Name
Ualloy142
Densitity
7.1
Elongtaion
>23(Annealing)
Max Working Temperature
1250
Magnetic Properties
Non-Magnetic
Ts
600~800MPa
Cr%
23~26%
Application
Electric Heating System
Raw Material
Fe-Cr-Al
Coefficient of Electric Resistance,
Low
Coil Weight
50kg
Transport Package
Standard Oversea Package
Specification
0.06 to 8mm
Trademark
Ualloy
Origin
China
Production Capacity
500t Per Month
Product Description
FeCrAl Heating Wire 0Cr25Al5 0.2mm to 8mm for TUBULAR COIL HEATERS in PET Preformed Moulds industry
Ualloy142B is a iron-chromium-aluminium alloy (FeCrAl alloy) characterized by high resistance, low coefficient of electric resistance, high operating temperature, good corrosion resistance under high temperature.It is suitable for use at temperatures up to 1250°C.
Typical applications for Ualloy142B are used in electric ceramic cooktop,industrial furnace,heaters.
Normal composition%
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
| Max | |||||||||
| 0.06 | 0.025 | 0.025 | 0.70 | Max 0.60 | 23.0~26.0 | Max 0.60 | 4.5~6.5 | Bal. | - |
Typical Mechanical properties(1.0mm)
| Yield strength | Tensile Strength | Elongation |
| Mpa | Mpa | % |
| 500 | 700 | 23 |
Typical Physical properties
| Density (g/cm3) | 7.10 |
| Electrical resistivity at 20ºC(ohmmm2/m) | 1.42 |
| Conductivity coefficient at 20ºC (WmK) | 13 |
| Coefficient of thermal expansion | |
| Temperature | Coefficient of Thermal Expansion x10-6/ºC |
| 20 ºC- 1000ºC | 15 |
| Specific heat capacity | |
| Temperature | 20ºC |
| J/gK | 0.46 |
| Melting point (ºC) | 1500 |
| Max continuous operating temperature in air (ºC) | 1250 |
| Magnetic properties | magnetic |
Temperature Factor of Electrical Resistivity
| 20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 500ºC | 600ºC | 700ºC | 800ºC | 900ºC | 1000ºC | 1100ºC | 1200ºC | 1300ºC |
| 1 | 1.002 | 1.005 | 1.008 | 1.013 | 1.021 | 1.030 | 1.038 | 1.040 | 1.042 | 1.044 | 1.046 | 1.047 |